1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
The present work shows AISI-SAE 1020 steel's nitrocarbide layer's microstructure and micro-hardness profile following 4 hours at 700ºC using methanol, isopropanol and triethanolamine. The steel was then hardened by quenching it in water and then tempered at 350ºC for 1 hour. Its surface had been par...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Artículo |
| Lenguaje: | inglés |
| Publicado: |
2005
|
| Materias: | |
| Acceso en línea: | https://dialnet.unirioja.es/servlet/oaiart?codigo=4902452 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares: 1020 AISI-SAE steel Austenitic Nitrocarburising with alcohol and triethanolamine
- Estabilidad térmica de recubrimientos de wc depositados por magnetrón sputtering dc
- Grapefruit (Citrus × paradisi) albedo debittering process for use in food industry
- Bactris guineensis, an underutilized Costa Rican palm fruit: Juice processing and its nutritional profile
- Optimización de la rugosidad y la dureza del acero 12l-14 empleando la metodología de superficie de respuesta
- Tratamientos de preservación de Bambusa vulgaris vittata contra el ataque de Dinoderus minutus
- Micromodeling of a dual-phase steel using an idealized micrograph generated by Voronoi diagrams