The corrosion resistance of 140MXC, 530AS and 560AS coatings produced by thermal spraying
Three commercial materials were deposited using electric arc thermal spraying: 140MXC (with Fe, W, Cr, Nb), 530AS (AISI 1015 steel) and 560AS (AISI 420 steel) on AISI 4340 steel. The aim of this paper was to evaluate the best strategy for improving a coating-substrate system’s corrosion resistance,...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Artículo |
| Lenguaje: | inglés |
| Publicado: |
2013
|
| Materias: | |
| Acceso en línea: | https://dialnet.unirioja.es/servlet/oaiart?codigo=4902648 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares: The corrosion resistance of 140MXC, 530AS and 560AS coatings produced by thermal spraying
- The effect of Ti(CN)/TiNb(CN) coating on erosion–corrosion resistance
- Corrosion resistance of Cu-Al coatings produced by thermal spray
- Unbalanced magnetron sputtering system for producing corrosion resistance multilayer coatings
- Estudio comparativo de la evaluación a la corrosión de recubrimientos de CrN y CrN/Cr con recubrimientos de cromo electrodepositado y pinturas tipo epoxy
- Protection against corrosion by molten salts through aluminum coatings deposited by arc thermal spray on ASTM A53 grade B steel
- Evaluación De La Capacidad Protectora De Recubrimientos Ni-SiC y Ni-Co-W Depositados Por Proyección Térmica