Microstructural evolution during austempering of a ASTM A-532 CLASS III type high chromium white cast iron undergoing abrasive wear

This paper studies the influence of variables such as holding temperatures and times during austempering of High Chromium White Cast Iron (HCWCI), with the following chemical composition: Cr 25 %, C 3 %, Si 0.47 %, Mn 0.74 % and Mo 1.02 %. The aim of the austempering was to modify the percentage of...

Descripción completa

Detalles Bibliográficos

Autores principales:	Higuera Cobos, Oscar Fabián, Bucurú Vasco, Jeison, Loaiza Patiño, Andrés Felipe, Monsalve, Mónica, Mesa Grajales, Dairo Hernán
Formato:	Artículo
Lenguaje:	inglés
Publicado:	2017
Materias:	Materials Engineering Austempered Retained austenite Abrasive wear High chromium white cast iron Chromium carbides Ingeniería de Materiales Austemperado Austenita retenida Desgaste abrasivo Fundiciones al alto cromo Carburos de cromo
Acceso en línea:	https://dialnet.unirioja.es/servlet/oaiart?codigo=6153104
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!