Investigation of Structural, Microstructural, Dielectrical and Magnetic Properties of Bi3+ Doped Manganese Spinel Ferrite Nanoparticles for Photonic Applications
The structural, microstructural, and magnetic properties of Mn1-xBixFe2O4 (where x = 0.0, 0.05, 0.1, 0.15, and 0.2) nanoparticles prepared by solution combustion method were investigated. Rietveld-refined X-ray diffraction patterns confirm the single-phase formation with space group Fd3m having spin...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | inglés |
| Publicado: |
IntechOpen
2020
|
| Materias: | |
| Acceso en línea: | https://www.intechopen.com/chapters/72254 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The structural, microstructural, and magnetic properties of Mn1-xBixFe2O4 (where x = 0.0, 0.05, 0.1, 0.15, and 0.2) nanoparticles prepared by solution combustion method were investigated. Rietveld-refined X-ray diffraction patterns confirm the single-phase formation with space group Fd3m having spinel cubic structure. The porous nature of the samples was confirmed by scanning electron microscopy (SEM). Composition values of the theoretical stoichiometry and energy-dispersive spectroscopy (EDS) composition values are well matched for all samples. The dielectric parameters such as real part of dielectric constant, imaginary part of dielectric constant, and dielectric loss tangent decrease with the increase in frequency. The AC conductivity increases with increase in the Bi3+ concentration. The real part of complex impedance decreases with the increase in frequency. Cole-Cole plots reveal that one semicircle was obtained for each of the samples. The real and imaginary parts of electric modulus vary with frequency. The magnetic hysteresis curves of all samples reveal the soft magnetic material nature. We observed S esteems began uniquely from the higher superparamagnetic, we would have watched the monotonic decrease in S with increase in Bi3+ concentration. Furthermore, the magnetic parameters were estimated. |
|---|---|
| ISBN: | 978-1-83968-242-1 |
| DOI: | 10.5772/intechopen.92430 |