Treatment Analysis of Welding Structure in the Presence of a Crack Type Defects
The largest number of welded structures in operating conditions is exposed to variable loads, which is why the share of fatigue fracture in the failure of welded structures is higher than others. The essence of construction with fracture safety is that the structure can withstand the designed load i...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | inglés |
| Publicado: |
IntechOpen
2020
|
| Materias: | |
| Acceso en línea: | https://www.intechopen.com/chapters/74178 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares: Treatment Analysis of Welding Structure in the Presence of a Crack Type Defects
- The Physics of Weld Bead Defects
- Welding Defect Detection with Deep Learning Architectures
- Comparative Analysis of Microstructural Assessment and Weld Defects in GMAW and GTAW Techniques
- Influence of Dissolved Hydrogen on Stress Corrosion Cracking Susceptibility of Nickel Based Weld Alloy
- Mitigating Zinc Vapor Induced Weld Defects in Laser Welding of Galvanized High-Strength Steel by Using Different Supplementary Means
- Physical Mechanisms and Mathematical Models of Bead Defects Formation During Arc Welding