Synthesis and Investigation of Ceramic Materials for Medium-Temperature Solid Oxide Fuel Cells
Finely dispersed (СeO2)1-x(Sm2O3)x (x = 0.02; 0.05; 0.10); La1-xSrxNiO3, La1-xSrxCoO3 and La1-xSrxFe0.7Ni0.3O3 (x = 0.30; 0.40) mesoporous xerogel powders are synthesized by co-crystallization of the corresponding nitrates with ultrasonic processing and used to obtain nanoscale ceramic materials wit...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | inglés |
| Publicado: |
IntechOpen
2022
|
| Materias: | |
| Acceso en línea: | https://www.intechopen.com/chapters/82028 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Finely dispersed (СeO2)1-x(Sm2O3)x (x = 0.02; 0.05; 0.10); La1-xSrxNiO3, La1-xSrxCoO3 and La1-xSrxFe0.7Ni0.3O3 (x = 0.30; 0.40) mesoporous xerogel powders are synthesized by co-crystallization of the corresponding nitrates with ultrasonic processing and used to obtain nanoscale ceramic materials with cubic fluorite-like, orthorhombic, and perovskite-like tetragonal crystal structure, respectively, with CSR ∼ 64–81 nm (1300°C). Physicochemical characterization of the obtained ceramics revealed that (СeO2)1-x(Sm2O3)x features with open porosity 2–6%, while for La1-xSrxNiO3, La1-xSrxCoO3, and La1-xSrxFe0.7Ni0.3O3, this value is about 21–29%. Ceria-based materials possess a predominantly ionic conductivity (ion transport numbers ti = 0.82–0.71 in the temperature range 300–700°C, σ700°С = 1.3·10−2 S/cm) determined by the formation of mobile oxygen vacancies upon heterovalent substitution of Sm3+ for Се4+. For solid solutions based on lanthanum nickelate and cobaltite, a mixed electronic-ionic conductivity (σ700°С = 0.80·10−1 S/cm) with ion transport numbers (te = 0.98–0.90, ti = 0.02–0.10) was obtained. The obtained ceramic materials are shown to be promising as solid oxide electrolytes and electrodes for medium-temperature fuel cells. |
|---|---|
| ISBN: | 978-1-80355-864-6 |
| DOI: | 10.5772/intechopen.105108 |