Dislocation-Point Defects-Induced by X-Irradiation Interaction in Alkali Halide Crystals
Strain-rate cycling tests under superposition of ultrasonic oscillation were carried out at 77–293 K for two kinds of samples: non-irradiated and X-ray-irradiated KBr single crystals. Point defects induced by X-ray irradiation have weak interaction with dislocation and act as obstacles to dislocatio...
Guardado en:
| Autor principal: | |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | inglés |
| Publicado: |
IntechOpen
2023
|
| Materias: | |
| Acceso en línea: | https://www.intechopen.com/chapters/87699 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares: Dislocation-Point Defects-Induced by X-Irradiation Interaction in Alkali Halide Crystals
- Luminescence of X-ray-Irradiated Single Crystals under the Influence of Compression
- Study on Influence of a State of Dopants on Dislocation-Dopant Ions Interaction in Annealed Crystals
- New Peak on Thermoluminescence Glow Curve of X-Ray-Irradiated Single Crystal after Heat Treatment
- Study on Dislocation-Dopant Ions Interaction during Plastic Deformation by Combination Method of Strain-Rate Cycling Tests and Application of Ultrasonic Oscillations
- Temperature Dependence of the Stress Due to Additives in KCl Single Crystals
- The Diffusion Model of Grown-In Microdefects Formation During Crystallization of Dislocation-Free Silicon Single Crystals