Investigation of Strain Effect on Cleavage Fracture for Reactor Pressure Vessel Material
Failure mechanism of 20MnMoNi55 steel in the lower self of ductile to brittle transition (DBT) region is considered as brittle fracture but it has been observed from the experimental analysis of stress-strain diagram that clear plastic deformation is shown by the material before failure. Therefore,...
Guardado en:
| Autor principal: | |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | inglés |
| Publicado: |
IntechOpen
2021
|
| Materias: | |
| Acceso en línea: | https://www.intechopen.com/chapters/79599 |
| Etiquetas: |
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares: Investigation of Strain Effect on Cleavage Fracture for Reactor Pressure Vessel Material
- Stress/Strain-Dependent Properties of Hydraulic Conductivity for Fractured Rocks
- Feed Water Line Cracking in Pressurized Water Reactor Plants
- Evaluating the Integrity of Pressure Pipelines by Fracture Mechanics
- Nuclear Thermal Propulsion Reactor Materials
- Flow Instability in Material Testing Reactors
- Fracture of Dental Materials