Investigation of Strain Effect on Cleavage Fracture for Reactor Pressure Vessel Material
Failure mechanism of 20MnMoNi55 steel in the lower self of ductile to brittle transition (DBT) region is considered as brittle fracture but it has been observed from the experimental analysis of stress-strain diagram that clear plastic deformation is shown by the material before failure. Therefore,...
Saved in:
| Main Author: | |
|---|---|
| Format: | Book Chapter |
| Language: | English |
| Published: |
IntechOpen
2021
|
| Subjects: | |
| Online Access: | https://www.intechopen.com/chapters/79599 |
| Tags: |
No Tags, Be the first to tag this record!
|
| Summary: | Failure mechanism of 20MnMoNi55 steel in the lower self of ductile to brittle transition (DBT) region is considered as brittle fracture but it has been observed from the experimental analysis of stress-strain diagram that clear plastic deformation is shown by the material before failure. Therefore, strain correction is implemented in the cleavage fracture model proposed by different researchers in the lower self of the DBT region with the help of finite element analysis. To avoid a huge number of experiments being performed, Monte Carlo simulation is used to generate a huge number of random data at different temperatures in the lower self of the DBT region for calibration of the cleavage parameters with the help of the master curve methodology. Fracture toughness calculated after strain correction through different models are validated with experimental results for the different probability of failures. |
|---|---|
| ISBN: | 978-1-83969-683-1 |
| DOI: | 10.5772/intechopen.101245 |